Legend:
| ✓ Ideally suited. | X Not suited. | ~ Not ideal, but can be used. |
| ECO | PRO | ECO+ PRO+ | ECO MAX PRO MAX | |
|---|---|---|---|---|
| Mixing Ratio by Weight Resin (A) : Hardener (B) | 100:50 | 100:50 | 100:50 | 100:50 |
| Applications | ||||
| Coating | ✓ | ✓ | ~ | ~ |
| Laminating | ✓ | ✓ | ~ | ~ |
| Sealing | ✓ | ✓ | ~ | ~ |
| Pouring | ~ | ✓ | ✓ | ✓ |
| Repairing | ✓ | ✓ | ~ | ~ |
| Glueing | ✓ | ~ | ~ | ~ |
| Application Areas | ||||
| Priming, Coating and Sealing of Floors (Industrial Floors, Garages, Interior Floors, Bath etc.) | ✓ | ✓ | X | X |
| Coating and Sealing of Tables, Countertops and Other Furniture/Objects | ✓ | ✓ | ~ | ~ |
| Sealing of Pictures | ✓ | ✓ | X | X |
| Pouring of Tables (River-Tables) | ~ | ~ | ✓ | ✓ |
| Creation of Jewellery and Small Castings up to 2cm Height | ✓ | ✓ | ~ | ~ |
| Casting of large pieces in one pour | X | X | ✓ | ✓ |
| Isolation of Electrical Circuits and Terminal Points | ✓ | X | X | X |
| Use in Aircraft, Ship and Model Construction | ✓ | ✓ | ~ | ~ |
| Bonding and Sealing of Concrete, Wood, Plastic, Hard Foam, Natural Stone, Fibreglass and Other Materials | ✓ | ~ | ~ | ~ |
| Processing Characteristics | ||||
| Wood Turning | ✓ | ✓ | ✓ | ✓ |
| Sandable | ✓ | ✓ | ✓ | ✓ |
| Polishable | ✓ | ✓ | ✓ | ✓ |
| Max. Pouring Height per Process1 | 1cm | 2cm | 5cm | 10cm |
| Waiting Time until Further Casting2 | 6h | 12h | 48-72h | 72-96h |
| Gelling Time and Pot Life | 25min (100g) | 65min (145g) | 6h (10kg) | 8h (10kg) |
| Min. Processing Temperature | 15°C | 15°C | 15°C | 15°C |
| Recommended processing temperature | 20°C | 20°C | 20°C | 20°C |
| Max. Relative Humidity during Processing | 70% | 70% | 70% | 70% |
| Max. Material Shrinkage | 1% | 1% | 1% | 1% |
| Processing Time (at 20°C) | ||||
| At Layer Height 0-3mm | 60min | 120min | 360min | 480min |
| At Layer Height 1cm | 25min | 90min | 360min | 480min |
| At Layer Height 2cm | X | 60min | 360min | 480min |
| At Layer Height 5cm | X | X | 240min | 360min |
| At Layer Height 10cm | X | X | X | 360min |
| Technical Properties | ||||
| Touchable / Accessible after | 24h | 24h | 48-72h | 96h |
| Completely Chemically Cured after | 7 days | 7 days | 14 days | 14 days |
| Transparent Resin | ✓ | ✓ | ✓ | ✓ |
| Crystal Clear Curing | X | ✓ | X (ECO+) ✓ (PRO+) | X (ECO M) ✓ (PRO M) |
| Max. Possible UV Stabilisation3 | X | ✓ | X (ECO+) ✓ (PRO+) | X (ECO M) ✓ (PRO M) |
| Self-Venting | ✓ | ✓ | ✓ | ✓ |
| Bubble Free | ✓ | ✓ | ✓ | ✓ |
| Self-Leveling | ✓ | ✓ | ✓ | ✓ |
| Solvent-Free | ✓ | ✓ | ✓ | ✓ |
| VOC Free4 | X | ✓ | X (ECO+) ✓ (PRO+) | X (ECO M) ✓ (PRO M) |
| BPA Free5 | ✓ | ✓ | ✓ | ✓ |
| Plasticiser Free (Phthalate) | ✓ | ✓ | ✓ | ✓ |
| Resistant to Chemicals | ✓ | ✓ | ✓ | ✓ |
| Scratch Resistant6 | ✓ | ✓ | ✓ | ✓ |
| Doming Effect (Depth Effect) | ✓ | ✓ | ✓ | ✓ |
| Miscible with all EPODEX Colours (Except WB PIGMENT) | ✓ | ✓ | ✓ | ✓ |
| Suitable for Underfloor Heating | ✓ | ✓ | ✓ | ✓ |
| Suitable for Outdoor Use | X | ✓ | X (ECO+) ✓ (PRO+) | X (ECO M) ✓ (PRO M) |
| High Adhesion | ✓ | ✓ | ✓ | ✓ |
| Density (g/cm)3 | 1.1 | 1.1 | 1.1 | 1.1 |
| Viscosity (mPa·s) | 700 | 530 | 350 | 350 |
| Max. Heat Deflection Temperature7 | 60°C | 60°C | 60°C | 60°C |
| Min. Heat Deflection Temperature | -30°C | -30°C | -30°C | -30°C |
| SHORE Hardness after Curing (D1) | 87 | 82 | 80 | 80 |
| Storage Temperature | 10-30°C | 15-30°C | 15-30°C | 15-30°C |
| Shelf Life | 12 Months | 12 Months | 12 Months | 12 Months |
| Shelf Life after Opening8 | 6 Months | 6 Months | 6 Months | 6 Months |
- Casting above the maximum pouring height per process is not recommended. The resin may boil as a result of the reaction and yellowing, cracking and deformation can occur. By reducing the temperature (room, substrate, material temperature to e.g. 15 °C and reducing the area to e.g. 15x15cm, casting heights of up to 50cm can be achieved in one casting process
- There is no maximum time limit to pour the next layer.
- No epoxy resin is completely UV stabilised. However, high-quality raw materials and additives such as UV absorbers can increase UV protection. By using a top coat, you can increase UV stabilisation even further. Possible top coats are e.g. transparent polyurethane (PU) resins or lacquers which are painted or sprayed onto the epoxy coating as a finish.
- When properly used and completely cured, it is VOC free..
- According to formula without free BPA.
- Our epoxy resin systems have a high scratch resistance, but are not completely scratch-resistant. Scratch resistance can be increased by using a top coat. Possible top coats are e.g. transparent polyurethane (PU) resins or lacquers which are painted or sprayed onto the epoxy coating as a finish.
- The heat deflection temperature indicates up to which temperature the cured epoxy resin system remains mechanically stable. At higher temperatures, the cured epoxy can soften. By annealing (curing at higher temperatures >60°C), the heat resistance can be increased.
- If the lid of the container is closed directly after opening, the shelf life after opening is at least 6 months.